Рулон встраиваемого токопроводящего пластика HIPS

В настоящее время, прозрачный лист PS и Ударопрочный лист PS are mostly processed by extrusion, thermoforming and injection molding.Many products also use blow molding and roll molding methods.

Most прозрачный лист PS и Ударопрочный лист PS are molded by extrusion, most of which are used to produce sheet.The sheet itself is saleable and is also used by the manufacturer for its own hot forming process.From building materials to corrugated plate and other products are available прозрачный лист PS и impact – resistant PS sheet extrusion molding.Extrusion molding of non-foaming products generally USES a two-stage exhaust extruder whose temperature ranges from 380°F(feeding section) to 430-460°F(extrusion section).New extrusion molding equipment, such as rotary extrusion molding machine, has been used.

Прозрачный лист PS и Ударопрочный лист PS are not absorbent, so they do not need to be dried before extrusion.However, if the temperature of the feed port is too low, or there is moisture on the surface of the pellet during storage, and the vent is blocked, then moisture becomes a problem.

Co-extrusion this is a rapidly developing process in which laminated products of the same or different plastics can be made.Прозрачный лист PS layer in the upper, impact resistant PS sheet for the lower co-extrusion molding products without adhesive bonding.Some layered structures, such as impact – resistant PS sheet coated with polyolefin plastic co-extrusion products need to be coated with adhesive bonding.

In the hot forming operation, the ratio of mixing recycled materials is 30~ 80%, some plastics can be through the extrusion machine 7 times or more repeatedly feed, прозрачный лист PS и impact resistant PS sheet can be repeatedly extruded, its performance does not significantly reduce.However, if the mixing of plastic with poor stability, even if the dosage is small, will cause a significant decline in performance.

Thermal forming is usually divided into four operations: conventional general forming, rotating station forming, tandem continuous thermal forming and continuous roll feeding forming.The thick sheet is heated by convection heating furnace and the thin sheet is heated by radiation furnace to soften it to the forming temperature.Molding process on the sheet quality requirements are very high, so in the extrusion process must be careful.

В настоящее время, прозрачный лист PS и Ударопрочный лист PS are the best size stability.The plastic with the shortest production cycle and lower cost is very suitable for many injection molding products.The barrel temperature is generally 390~500°F.In order to shorten the production cycle and improve product quality, injection molding systems with ultra-fast injection and recovery rates have been developed.A variety of molds are used in processing plants, including hot runner systems and various forms of gate design.

Different foaming agents, such as pentane, nitrogen, CBA and freon, should be used for foam molding and extrusion of прозрачный лист PS и Ударопрочный лист PS.According to the purpose of the additives can reach more than 10 kinds, also may not be added.

The formation of hair – able полистирол is divided into two sections: the first polystyrene particles prehair foam to make it into a prehair.Precursors are usually aged to allow air to seep into the pores and to replace the foaming agent and water in the pores.Then the pre-foaming beads after curing are sent to the mold with steam channel for hot forming, and the final product is obtained.This method can be used to produce thin wall products (cups) or foam blocks of 2ft*16ft*4ft, and then cut into slats of 4ft*8ft *1(or > 1)in, which can be used for insulation.The density of recoverable полистирол can vary from less than 1ib/ft3 to more than 6 lb/ft3.

Parameters of Embedded Conductive HIPS Plastic Roll

Прозрачный лист PS granule is an amorphous polymer obtained by addition polymerization of styrene monomer.Colorless, transparent, excellent optical performance, and high rigidity.The properties of прозрачный лист PS следующие:

The density of 1.05 g/cm3

The tensile strength is 48.3MPa.

The bending strength is 82.7MPa.

The typical shrinkage is 0.0045 in/in

Thermal expansion coefficient 5-8 X 10-5in/(in·°c)

Elongation is 2-3%

Vica softening point 225°F

Полистирол itself is resistant to y rays, so y line irradiation sterilization has no effect on product performance. Полистирол dissolves in aromatic solvents and certain ketones and is soluble in methyl ethyl ketones.The melt index range of прозрачный лист PS particles is 1-25 g/10 min or higher than 25 g/10 min.It has high heat resistant grades (vica softening point up to 223°F) and low residual monomer content grades.